純Ａｌ／炭素鋼クラッド材の接合部特性と微細構造の観察―真空圧延接合法によるクラッド材の製造とその特性（第５報）―

• 山口 富子

  九州工業大学

• 西尾 一政

  九州工業大学

• 加藤 光昭

  九州工業大学

• 黒川 哲平

  九州工業大学大学院（現在東洋鋼鈑（株））

書誌事項

タイトル別名

• Properties and HR-TEM Observations of Al/ Mild Steel Clad Materials-Development of Clad Materials by Vacuum Roll Bonding and its Characteristics (part 5)-
• Properties and HR-TEM Observations of Al/ Mild Steel Clad Materials
• —Development of Clad Materials by Vacuum Roll Bonding and its Characteristics (part 5)—
• ―真空圧延接合法によるクラッド材の製造とその特性（第5報）―

抄録

We hold many expectations that aluminum-clad steel will be applied for functional material, structural transition joint for welding steel structure to aluminum structure and so on. In this study we investigated the effects of aluminum purity and/or bonding conditions, which were bonding temperature, reduction rate of aluminum plate thickness (RAl), vacuum degree, on bond tensile strength of aluminum-clad steels produced by the vacuum roll bonding. And also the bond interfaces were observed using a high-resolution transmission electron microscope (RE-TEM).<br>When A1050/SS400 clad materials, which produced at more than 450°C in bonding temperature, more than 17% in R_Al and less than 10 Pa in vacuum degree, were performed in tensile test, they fractured through base metal of the aluminum. The values of bond tensile strength were obtained over 100 MPa. The bond tensile strength of 4N-Al (99.99 mass%Al) /SS400 clad material, which produced at 500°C in bonding temperature, 20% in R_Al and 3 Pa in vacuum degree, was obtained about 80 MPa and test piece fractured through base metal of the aluminum. In the analysis results for bond interface of A1050/SS400 clad materials (500°C in bonding temperature, 20% in R_Al and 3 and 10 Pa in vacuum degree) using a HR-TEM and an electron dispersive spectroscopy (EDS), no intermetallic compound and continuously amorphous phase in thickness from 2 to 3 nm were observed. The composition of the amorphous phase consists of mostly Al, O, Fe and Si. For the bonding interface of 4N-Al/SS400 clad material (500°C in bonding temperature, 20% in R_Al and 3 Pa in vacuum degree), amorphous phase and nano-crystal were observed using HR-TEM. Therefore, it was clarified A1050 and 4N-Al/SS400 clad materials obtained using a vacuum roll bonding were bonded through the amorphous phase.

収録刊行物

• 溶接学会論文集

  溶接学会論文集 24 (3), 215-222, 2006

  一般社団法人 溶接学会

キーワード

• Aluminum-clad steel
• Vacuum roll bonding
• Amorphous phase
• Nano-crystal
• Bond tensile strength
• Clad material

詳細情報

• CRID: 1390001204727381248
• NII論文ID: 130004445482
• DOI: 10.2207/qjjws.24.215
• COI: 1:CAS:528:DC%2BD28XhtVyhsLnL
• ISSN: 24348252
• ISSN: 02884771
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可