レーザ照射によるオーステナイト系ステンレス鋼の結晶粒微細化

書誌事項

タイトル別名
  • Grain Refinement of Austenitic Stainless Steel by Laser Irradiation

この論文をさがす

抄録

In structural materials, it is investigated to make crystal grain size less than 1μm in order to improve strength and toughness. Authors reported that fine ferrites were obtained by laser irradiation in steel. However, it is not made clear that an effect of laser irradiation on the materials which do not have a transformation. In this study, we performed laser irradiation for austenite stainless steel SUS304 as the materials which did not have a transformation and investigated an effect of laser irradiation on grain refinement. Solution treatments were performed for SUS304 and their initial grain size became 23 and 68μm. Then they were given four kinds of strain ε and irradiated laser under some laser traveling speeds ν and some defocus distances ƒd. As the result, they became recrystallization grain and their size were obtained about 10 and 15μm, for initial grain size respectively, under the best condition (laser power=1.5kW, fd=60mm, v=350 mm/min, ε= 40%). Then a recrystallization grain size was caused by each factor of laser traveling speed (heating temperature, heating time), strain and defocus distance. Furthermore, as an electro-gas arc weld of SUS304, the grain size was 40μm in heat affected zone, was irradiated after shot peening, it was clarified that fine grain was obtained from 10 to 15μm at the heat affected zone.

収録刊行物

参考文献 (2)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ