Fatigue Behavior of Ceramic Matrix Composite Oxidized at Intermediate Temperatures
-
- Zhu Shijie
- Department of Intelligent Mechanical Engineering, Fukuoka Institute of Technology
この論文をさがす
抄録
The effect of intermediate temperature oxidation on fatigue behavior of SiC/SiC is investigated to understand fatigue damage mechanisms. It has been found that fatigue life is decreased by 13% after oxidation at 600°C for 100 hours due to disappearance of carbon interphase by oxidation. The strong bonding between the fibers and matrix caused by SiO2 formation at 800°C for 100 hours leads to the shortest fatigue life.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (8), 1965-1967, 2006
公益社団法人 日本金属学会