Formation and mechanical properties of Mg97Zn1RE2 alloys with long-period stacking ordered structure
-
- Kawamura Yoshihito
- Department of Materials Science and Engineering, Kumamoto University
-
- Yamasaki Michiaki
- Department of Materials Science and Engineering, Kumamoto University
書誌事項
- タイトル別名
-
- Formation and Mechanical Properties of Mg<SUB>97</SUB>Zn<SUB>1</SUB>RE<SUB>2</SUB> Alloys with Long-Period Stacking Ordered Structure
- Formation and mechanical properties of Mg85Zn1RE2 alloys with long period stacking ordered structure
- Formation and mechanical properties of Mg97Zn1RE2 alloy with long-period stacking ordered structure
この論文をさがす
抄録
We investigated the formation and mechanical properties of Mg97Zn1RE2 alloys with long-period stacking ordered (LPSO) structures by examining RE = Y, La, Ce, Pr, Sm, Nd, Gd, Dy, Ho, Er, Tb, Tm and Yb. The LPSO phase developed for RE = Y, Dy, Ho, Er, Gd, Tb and Tm. LPSO Mg-Zn-RE alloys are either type I, in which the LPSO phase forms during solidification: Mg-Zn-Y, Mg-Zn-Dy, Mg-Zn-Ho, Mg-Zn-Er and Mg-Zn-Tm, or type II, in which the LPSO phase is nonexistent in as-cast ingots but precipitates with soaking at 773 K: Mg-Zn-Gd and Mg-Zn-Tb. The criteria for REs that form an LPSO phase in Mg-Zn-RE alloys are discussed. Mg-Zn-RE alloys with an LPSO phase, which were worked by hot extrusion, include high strength both at ambient and elevated temperatures, and good ductility. Their tensile yield strength, ultimate strength and elongation were 342–377 MPa, 372–410 MPa and 3–9%, respectively at ambient temperature, and 292–310 MPa, 322–345 MPa and 4–13% at 473 K. The LPSO Mg-Zn-RE alloys are promising candidates for lightweight structural materials.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (11), 2986-2992, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250060288
-
- NII論文ID
- 10019789726
- 130004453425
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD1cXkt1entA%3D%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8979552
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可