- Fabrication of Nb3Al Wires by the Clad-Chip Extrusion Method and the Rapid-Heating, Quenching and Transformation Treatment and Their Superconducting Properties
抄録
This paper describes a fabrication process of Nb3Al intermetallic compound wires and measurements of their superconducting properties. Nb3Al superconducting wires are successfully fabricated by the combined process of the clad-chip extrusion (CCE) method and the rapid-heating, quenching and transformation (RHQT) treatment. The CCE method is a processing of Nb/Al composite wire with fine-layered structure, which is characterized by the extrusion of thin chips of clad-rolled Nb/Al sheet. Its chemical composition is controlled by the thickness ratio of the Nb-layer to the Al-layer at clad-rolling. The RHQT treatment is a heat-treatment to convert the Nb/Al composite into Nb3Al, which can produce fine grain structure of Nb3Al intermetallic compound with nearly stoichiometric composition. It is favorable for upgrading the superconducting properties.<BR>The critical transition temperature and the critical current density are enhanced by optimizing the microstructure of the CCE-processed precursor wire and the transformation condition in the RHQT process. Plastic working of the bcc supersaturated solid solution wire after rapid-heating and quenching is found to be effective for enhancing the critical current density in high magnetic field.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 68 (9), 629-635, 2004
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681453985280
-
- NII論文ID
- 130004455501
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可