ＳＵＳ３０４のＭｇＣｌ２液滴中における腐食過程のその場観察とＡＥ源の検討

• 志波 光晴

  独立行政法人物質・材料研究機構

• 升田 博之

  独立行政法人物質・材料研究機構

• 山脇 寿

  独立行政法人物質・材料研究機構

• 伊藤 海太

  東京大学大学院工学研究科マテリアル工学専攻

• 榎 学

  東京大学大学院工学研究科マテリアル工学専攻

書誌事項

タイトル別名

• In-Situ Observation and Acoustic Emission Analysis for Corrosion Pitting of MgCl2 Droplet in SUS304 Stainless Steel

抄録

  Acoustic emission with near-field detection and optical video microscope monitoring was proposed to investigate the pitting corrosion caused by the small magnesium chloride droplet. For the corrosion testing of work-hardened SUS304 stainless steel, four types of the detected waveforms were characterized by the wavelet analysis. After the high activity AE signals, the corrosion product sheet was extended without or with low activity AE signals. With the cross-section observations, the detected AE signals were mainly attributed to the following three sources, the longitudinal and transverse cracking around the covered pitting, cracking of the oxidation products, and the early stage of the corrosion potential fluctuation.<br>

収録刊行物

• 日本金属学会誌

  日本金属学会誌 76 (2), 122-128, 2012

  公益社団法人 日本金属学会

キーワード

• corrosion
• droplet
• SUS304
• acoustic emission
• <i>in-situ</i> optical observation

詳細情報

• CRID: 1390001206481795712
• NII論文ID: 130004456273
• DOI: 10.2320/jinstmet.76.122
• COI: 1:CAS:528:DC%2BC38XltFShtrw%3D
• ISSN: 18806880
• ISSN: 24337501
• ISSN: 00214876
• Web Site: https://www.jstage.jst.go.jp/article/jinstmet/76/2/76_2_122/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
  • KAKEN
• 抄録ライセンスフラグ: 使用不可