Lead-free Li-modified (Na,K)NbO<sub>3</sub> piezoelectric ceramics fabricated by two-step sintering method
-
- KATO Kensuke
- Department of Materials Science and Engineering, Graduate School of Engineering, Nagoya Institute of Technology
-
- KAKIMOTO Ken-ichi
- Department of Materials Science and Engineering, Graduate School of Engineering, Nagoya Institute of Technology
-
- HATANO Keiichi
- Materials R&D Department, R&D Laboratory, Taiyo Yuden Co., Ltd.
-
- KOBAYASHI Keisuke
- Materials R&D Department, R&D Laboratory, Taiyo Yuden Co., Ltd.
-
- DOSHIDA Yutaka
- Materials R&D Department, R&D Laboratory, Taiyo Yuden Co., Ltd.
Abstract
Two-step sintering method has been applied to (Li0.06Na0.47K0.47)NbO3 (LNKN) ceramics in order to obtain a homogenous microstructure and high density (96.1% TD). The effects of the sintering temperature on the microstructure and electrical properties of LNKN ceramics were investigated. The two-step sintering has provided better densification at relatively lower temperature (≦950°C) than that of one-step sintering (1082°C), which suppresses the abnormal grain growth. In addition, the more homogeneous microstructure has been obtained by two-step sintering. The measured dielectric constant, dielectric loss and Curie temperature of the sample for two-step sintering were 666, 2.0% and 454°C, respectively, similar to the values obtained with one-step sintering. Nevertheless, LNKN ceramics prepared by two-step sintering showed higher coercive electric field (=18.8 kV/cm) than that revealed by one-step sintering (=13.0 kV/cm).
Journal
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 122 (1426), 460-463, 2014
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680263959680
-
- NII Article ID
- 130004480252
-
- ISSN
- 13486535
- 18820743
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed