- Improvement of Corrosion Resistance in Austenitic Stainless Steel by Grain Boundary Character Distribution Control
抄録
Strauss test, Coriou test and Huey test were conducted on a Type 316L austenitic stainless steel. Improvement in grain boundary corrosion resistance was verified after raising low Σ coincidence site lattice (CSL) grain boundary (GB) frequency by controlling grain boundary character distribution (GBCD). During crevice corrosion test under gamma-ray irradiation, initiation frequency of GB corrosion after GBCD controlled specimens decreased to 1/10 of GBCD uncontrolled counterpart along with lower depth of corrosion. Stress corrosion cracking (SCC) propagation rate of GBCD controlled specimen decreased to less than 1/2 of GBCD uncontrolled specimen in high temperature and high pressure water. Based on these results, we expect that GBCD control will improve corrosion resistance of austenitic material in a wide range of application and environment.
収録刊行物
-
- Zairyo‐to‐Kankyo
-
Zairyo‐to‐Kankyo 61 (9), 359-365, 2012
公益社団法人 腐食防食学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206259107968
-
- NII論文ID
- 130004503132
-
- COI
- 1:CAS:528:DC%2BC38XhsFOnu7bL
-
- ISSN
- 18819664
- 09170480
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可