Crystal Structures of Cobalt-Exchanged Sodium GTS-type Titanosilicates and the Elution Test by Acid Solution
-
- Fujiwara K.
- Graduate School of Science and Engineering,Yamaguchi Univ.
-
- Tamaki T.
- Graduate School of Science and Engineering,Yamaguchi Univ.
-
- Kishimori C.
- Graduate School of Science and Engineering,Yamaguchi Univ.
-
- Titorenkova R.
- Graduate School of Science and Engineering,Yamaguchi Univ.
-
- Nakatsuka A.
- Graduate School of Science and Engineering,Yamaguchi Univ.
-
- Nakayama N.
- Graduate School of Science and Engineering,Yamaguchi Univ.
抄録
Fine particles of Na-GTS have been prepared by using hydrothermal method. Co2+-exchanged GTS were obtained by shaking 0.5 g of the single-phase Na-GTS sample in the aqueous solutions of CoCl2 (25 mL, 0.025~1.0 M) at 40℃ for 24 hours. Samples with the composition 0.23 ≤ x ≤ 0.9 in the formula of Na4-4xCo2xTi4Si3O16 were obtained. With the increase of Co composition x, the rhombohedral lattice parameter a increases and α becomes close to 90°. The Co elution ratios were about 90 % for the samples with x = 0.23 and 0.56, whereas 70% for the samples of ion exchange ratio with x = 0.88. By Co2+ exchange, the water content increased from 20.5 to 24.5 % and the DTA peak temperature due to the dehydration was lowered from 253 to 230℃. FT-IR spectra showed apparent change in the absorption peaks due to the O-H stretching in the range of 3000~3600 cm-1 suggesting some change in the hydration state.
収録刊行物
-
- Transactions of the Materials Research Society of Japan
-
Transactions of the Materials Research Society of Japan 38 (3), 455-458, 2013
一般社団法人 日本MRS
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205512183424
-
- NII論文ID
- 130004676466
-
- COI
- 1:CAS:528:DC%2BC3sXhvVyjtLnJ
-
- ISSN
- 21881650
- 13823469
- http://id.crossref.org/issn/13823469
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可