ジルコニアオールセラミック修復用ベニアポーセレンの破壊靱性に関する研究:―フレーム材とポーセレンの焼成条件の影響―  [in Japanese] Fracture Toughness of Veneer Porcelain for Zirconia All-Ceramic Restorations:— Influence of the Frame Materials and Porcelain Firing Schedules —  [in Japanese]

Access this Article

Search this Article

Author(s)

    • 工藤 桃子 Kudo Momoko
    • 東北大学大学院歯学研究科咬合機能再建学分野 Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University
    • 三浦 賞子 Miura Shoko
    • 東北大学大学院歯学研究科咬合機能再建学分野 Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University
    • 菊地 聖史 Kikuchi Masafumi
    • 鹿児島大学大学院医歯学総合研究科歯科生体材料学分野 Division of Biomaterials Science, Graduate School of Medical and Dental Sciences, Kagoshima University
    • 稲垣 亮一 Inagaki Ryoichi
    • 東北大学大学院歯学研究科咬合機能再建学分野 Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University
    • 笠原 紳 Kasahara Shin
    • 東北大学大学院歯学研究科咬合機能再建学分野 Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University
    • 佐々木 啓一 Sasaki Keiichi
    • 東北大学大学院歯学研究科口腔システム補綴学分野 Division of Advanced Prosthetic Dentistry, Graduate School of Dentistry, Tohoku University
    • 依田 正信 Yoda Masanobu
    • 東北大学大学院歯学研究科咬合機能再建学分野 Division of Fixed Prosthodontics, Graduate School of Dentistry, Tohoku University

Abstract

<b>目的</b>:本研究の目的は,ジルコニアフレームや焼成条件の変化がベニアポーセレンの機械的性質に及ぼす影響を調べるため,フレーム材料,焼成温度,昇温速度による破壊靱性を検討することである.<br><b>方法</b>:破壊靱性値の測定は,ISO15732に準じた破壊靭性試験により評価した.ジルコニアオール<br>セラミック修復用ベニアポーセレンは,2種類の異なった厚さのジルコニアフレーム(以下ZAC)に,各3条件の焼成温度及び昇温速度にて焼成した.コントロールとして,メタルセラミック修復用ベニアポーセレン及びメタルフレーム(以下PFM)を使用した.データは,2-way ANOVA Tukey-Kramer HSD test(<i>α</i>=0.05)にて統計分析を行った.<br><b>結果</b>:ZAC及びPFMの破壊靱性値は,フレーム厚さの違いや焼成温度条件では有意差はみられなかった.昇温速度条件では,ZACでは速度を速くした場合においてマニュアル条件よりも破壊靱性値は有意に低くなった(p<0.05).また,PFMでは速度を遅くした場合においてマニュアル条件及び速い条件よりも破壊靱性値は有意に高い値となった(p<0.05).<br><b>結論</b>:ジルコニアオールセラミック修復用ベニアポーセレンの破壊靭性値は,フレーム厚さの違いや焼成温度による影響はみられなかったが,昇温速度を速くした場合において,有意に低い値となった.

<b>Purpose: </b>We investigated how various frame materials, porcelain firing temperature and heating rate influenced the fracture toughness of the veneer porcelain used for zirconia all-ceramic restorations.<br><b>Methods:</b> The fracture toughness was evaluated according to the ISO 15732 standard. The veneer porcelain for the zirconia all-ceramic restorations was fired on 0.4- and 0.8-mm-thick zirconia frames (ZAC) at moderate firing schedules, and fired on ZAC(0.4) at low, moderate, and high temperatures and at slow, moderate, and fast heating rates. Veneer porcelain fired on metal frames for porcelain-fused-to-metal (PFM) ceramic restorations was also evaluated as a control. The data were analyzed using 2-way ANOVA and the Tukey-Kramer HSD test (<i>ɑ</i> = 0.05).<br><b>Results:<br></b> The effects of the ZAC and PFM frame thicknesses and the firing temperature on the fracture toughness of the veneer porcelain were not significantly different. The fracture toughness of the sample heated fast on the ZAC was significantly lower than that of the samples heated at slow and moderate rates (<i>p</i> < 0.05). The fracture toughness of the sample heated slowly on the PFM was significantly higher than that of the samples heated at moderate and fast rates (<i>p</i> < 0.05).<br><b>Conclusions:</b> The results suggest that the effects of the ZAC frame thickness and firing temperature on the fracture toughness of the veneer porcelain were not significantly different; however, the heating rate significantly influenced the fracture toughness.

Journal

  • Annals of Japan Prosthodontic Society

    Annals of Japan Prosthodontic Society 6(3), 291-299, 2014