Structure of Iron-Based Cladding Layer on Al-Mg-Si Alloy Coated by a Resistance Seam Welding Method
-
- Wang Wenqin
- Department of Materials and Science, Kyushu Institute of Technology
-
- Yamaguchi Tomiko
- Department of Materials and Science, Kyushu Institute of Technology
-
- Nishio Kazumasa
- Nishinippon Institute of Technology
この論文をさがす
抄録
Iron-based cladding layers were successfully fabricated on the 2 mm thick Al-Mg-Si (A6061) alloys to improve the wear resistance of the substrate by a resistance seam welding (RSEW) method. Microstructure showed that the cladding layer consisted of the high carbon iron alloy powders (SHA) reinforcement, A6061 binder and Fe-Al phases. The Fe-Al phases had two kinds of micro-structured morphologies: a needle-like phase in the A6061 identified as FeAl3, and a planer transition phase at the A6061/SHA powders interface identified as Fe2Al5 and FeAl3. A ball-on-disc test was carried out to evaluate the wear resistance of the cladding layers and the wear mechanism was discussed by observing the worn surfaces. Furthermore, the relationship of welding current and the microstructure, as well as the wear resistance of the cladding layer, were also investigated. The results showed that the wear resistance of the cladding layer increased with the increase of the welding current and the best wear performance was found at the welding current of 3.0 kA, where the wear rate was near two orders of magnitude less than the substrate. It was also suggested that the FeAl3 in the cladding layer had a critical role to improve the wear resistance. Moreover, the wear mechanisms of the cladding layer changed from adhesion and delaminate to adhesion with the increase of the welding current.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (11), 1698-1706, 2014
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679228885248
-
- NII論文ID
- 130004694473
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025890591
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可