コンクリート中における亜硝酸イオンの腐食抑制メカニズムおよびその効果に関する基礎的研究  [in Japanese] Basic Study on Corrosion Controlling Mechanism of Nitrite Ion and Its Effectiveness in Concrete  [in Japanese]

Access this Article

Search this Article

Author(s)

Abstract

Lithium nitrite injection method has been employed in recent years to prevent ASR due to the presence of lithium ion. Meanwhile, in the presence of nitrite ion, lithium nitrite is also expected to inhibit steel corrosion in concrete when water, oxygen and chloride ion may ingress through ASR-induced cracks. Consequently, lithium nitrite is applied to repair concrete section either combined in patching material or being a coating material. Despite of its widespread application, quite a few problems on corrosion-inhibiting mechanism of nitrite ion have not been fully understood yet. How to evaluate the effect of nitrite ion and its related risk of macro-cell corrosion is among them. Purpose of this study is to investigate the corrosion-inhibiting mechanism of nitrite ion based on polarization tests of steel bars corroded under various kinds of corrosion conditions. A further discussion on the application of nitrite ion is present upon the test results.

Journal

  • Journal of the Society of Materials Science, Japan

    Journal of the Society of Materials Science, Japan 63(10), 722-728, 2014

    The Society of Materials Science, Japan

Codes

  • NII Article ID (NAID)
    130004699362
  • NII NACSIS-CAT ID (NCID)
    AN00096175
  • Text Lang
    JPN
  • ISSN
    0514-5163
  • NDL Article ID
    025872378
  • NDL Call No.
    Z14-267
  • Data Source
    NDL  J-STAGE 
Page Top