PREPARATION OF POROUS SPHERICAL HYDROXYAPATITE AGGLOMERATES INTERACTED WITH CYCLODEXTRIN
-
- ITATANI Kiyoshi
- Department of Materials and Life Sciences, Faculty of Science and Engineering, Sophia University
-
- IKEGAMI Sayaka
- Department of Materials and Life Sciences, Faculty of Science and Engineering, Sophia University
-
- HAYASHITA Takashi
- Department of Materials and Life Sciences, Faculty of Science and Engineering, Sophia University
-
- DAVIES Ian J.
- Department of Mechanical Engineering, Curtin University of Technology
-
- UMEDA Tomohiro
- Department of Materials and Life Sciences, Faculty of Science and Engineering, Sophia University
-
- MUSHA Yoshiro
- 2nd Department of Orthopaedic Surgery, School of Medicine, Toho University
-
- KODA Seiichiro
- Department of Materials and Life Sciences, Faculty of Science and Engineering, Sophia University
抄録
Porous spherical hydroxyapatite (Ca10(PO4)6(OH)2: HAp) agglomerates with diameters of approximately 1 µm were prepared by: (i) the spray-pyrolysis of calcium phosphate solution containing 0.5 mol dm-3 Ca(NO3)2, 0.3 mol dm-3 (NH4)2HPO4, 0.1 - 0.4 mol dm-3 glutaric acid and concentrated HNO3 at 600°C, using an ultrasonic vibrator, and then (ii) the burnout of residual carbon resulting from the pyrolysis of glutaric acid upon the heat treatment of the spray–pyrolyzed powder at 900°C for 10 min. Three types of resulting HAp powders were then hydrothermally treated with 1.5 mass% β-cyclodextrin (β-CyD) solution at 120°C for 1 h. The amounts of β-CyD in the resulting HAp agglomerates were found to be in the range of 1.1 to 13.1 mass%. Transmission electron microscopy confirmed the presence of β-CyD not only on the surfaces but also inside the spherical HAp agglomerates. When the HAp powder with 13.1 mass% β-CyD addition was immersed in pure water at 90°C for 1 h, the released amount of β-CyD was as low as 2.1 mass%, indicating the enhanced chemical bonding between β-CyD and HAp, due to the hydrothermal treatment.
収録刊行物
-
- Phosphorus Research Bulletin
-
Phosphorus Research Bulletin 24 54-61, 2010
日本無機リン化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205287693440
-
- NII論文ID
- 130004726107
-
- ISSN
- 18822363
- 09184783
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可