Influence of Co on Strength and Microstructure of Cu-Ni-Co-Si Alloy
-
- IZAWA Kotaro
- Graduate Studeent, Div. of Mech. Sci. and Eng., Kanazawa Univ.
-
- OZAWA Atsushi
- Graduate Studeent, Div. of Mech. Sci. and Eng., Kanazawa Univ.
-
- KITA Kazuhisa
- Div. of lnnovation Tech. and Sci., Kanazawa Univ.
-
- WATANABE Chihiro
- Div. of lnnovation Tech. and Sci., Kanazawa Univ.
-
- MONZEN Ryoichi
- Div. of lnnovation Tech. and Sci., Kanazawa Univ.
Bibliographic Information
- Other Title
-
- Cu-Ni-Co-Si合金の強度と組織に及ぼすCoの影響
- Cu-Ni-Co-Si ゴウキン ノ キョウド ト ソシキ ニ オヨボス Co ノ エイキョウ
Search this article
Abstract
Cu-2.0wt%Ni-0.5wt%Si, Cu-1.4wt%Ni-0.6wt%Co-0.5wt%Si (0.6%Co) and Cu-1.0wt%Ni-1.0wt%Co-0.5wt%Si (1.0%Co) alloys produced by combining cold rolling to a 25% and a 90% reduction with aging treatment are employed to investigate the effects of Co on the strength and microstructure of Cu-Ni-Co-Si alloys. Aging the 0.6%Co and 1.0%Co alloys at 525, 425 and 325℃ produces orthorhombic (Ni, Co)2Si precipitates that have the same crystal system as Ni2Si precipitates formed in the 0%Co alloy. The larger the amount of Co in the three alloys is, the higher the dislocation density in the alloys peak-aged and rolled to a 25% and a 90% reduction is. The amounts of deformation twins observed in the 0.6%Co and 1.0%Co alloys peak-aged at 525℃ and rolled to a 90% reduction are much larger than that observed in the 0%Co alloy peak-aged at 525℃ and rolled to a 90% reduction. The strength and electrical conductivity of the three alloys initially aged at 525℃, rolled to a 25% reduction and re-aged at 425℃ (A25RA), or aged at 525℃, rolled to a 90% reduction and re-aged at 325℃ (A90RA) becomes higher as the Co content increases. The increase in strength with increasing the Co content is attributed to decrease in the inter-precipitate spacing and increase in the dislocation density for the A25RA alloys, and increase in the amount of deformation twins in addition to decrease in the inter-precipitate spacing and increase in the dislocation density for the A90RA alloys.
Journal
-
- Journal of the Society of Materials Science, Japan
-
Journal of the Society of Materials Science, Japan 63 (5), 401-408, 2014
The Society of Materials Science, Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680421640448
-
- NII Article ID
- 130004749897
-
- NII Book ID
- AA11556898
-
- ISSN
- 18807488
- 05145163
-
- NDL BIB ID
- 025547106
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed