Intergranular Segregation in the Pressure Vessel Steel of a Commercial Nuclear Reactor Studied by Atom Probe Tomography
-
- Toyama Takeshi
- International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University
-
- Nagai Yasuyoshi
- International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University
-
- Al Mazouzi Abderrahim
- SCK-CEN, Nuclear Materials Science Institute
-
- Hatakeyama Masahiko
- International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University
-
- Hasegawa Masayuki
- International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University
-
- Ohkubo Tadakatsu
- National Institute for Materials Science
-
- Van Walle Eric
- SCK-CEN, Nuclear Materials Science Institute
-
- Gerard Robert
- Tractebel Engineering
この論文をさがす
抄録
Solute/impurity segregation and precipitation at grain boundaries (GBs) in a nuclear reactor pressure vessel (RPV) steel were investigated using laser-assisted atom probe tomography (APT): RPV surveillance test specimens irradiated in a commercial nuclear reactor to neutron doses of 0.83 × 1019 n·cm−2 (low-dose) and 5.1 × 1019 n·cm−2 (high-dose), corresponding to in-service exposure of ∼5 and ∼30 years, respectively. The segregation of C, P and Mo was found on GBs after the low-dose irradiation. The segregation of Si and Mn as well as C, P and Mo was observed after the high-dose irradiation. The monolayer coverage of P is estimated to be less than a suggested level for intergranular embrittlement. The segregation of C, P and Mo was also observed along parallel array of dislocation lines in small-angle grain boundaries. However, no segregation of Si and Mn was detected there. Copper-nano precipitates (CNPs) were observed on the GBs, along the dislocation lines and in the matrix. The sizes and the solute-impurity enrichment in these CNPs are compared.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (11), 2119-2124, 2013
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679226108544
-
- NII論文ID
- 130004824987
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC2cXhvFaiug%3D%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 024968808
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可