Fabrication and evaluation of hybrid materials from A-zeolite and ground glass powders for vitrified radioactive waste
-
- KAMITANI Masataka
- Makino Corporation Osaka Prefecture University
-
- TAGAMI Toru
- Osaka Prefecture University
-
- KONDO Mitsunori
- Makino Corporation
-
- HIKI Tomonori
- Makino Corporation
-
- WAKIHARA Toru
- The University of Tokyo
-
- NAKAHIRA Atsushi
- Osaka Prefecture University Tohoku University, IMR, Kansai-Center
Abstract
The samples from A-type zeolite and ground soda-lime glass powders were solidifed by calcinations at 600 to 800°C in air atmosphere. These hybrid zeolite/glass samples at 700°C were in part insufficiently densified and hybrid samples were fully densified at 800°C, although the densification was not generated at 600°C. A-zeolites were still stable in glass melt at 800°C for hybrid zeolite/glass samples. These hybrid zeolite/glass samples had the ion exchange ability of 20% against Sr2+ and the high ability over 80% against Cs+ as well as A-zeolite. Microstructures of obtained hybrid zeolite/glass samples were evaluated.
Journal
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 122 (1422), 151-155, 2014
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205287883392
-
- NII Article ID
- 130004950925
-
- ISSN
- 13486535
- 18820743
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed