抄録
Hydroxyapatite was precipitated from a supersaturated solution of Ca(OH)2 by neutralization with orthophosphoric acid. This precipitation led to a suspension of fine particles. The influence of the operating conditions was established experimentally. The suspension of hydroxyapatite particles was directly dried by fluidization on a support. The feasibility of the fluidization process was studied and the main parameters determined : support (glass balls, φ : 530 μm), temperature of drying air, method of introduction of the pulp. The final product is a fine powder of hydroxyapatite with a median diameter in the range 63 - 100 μm.
収録刊行物
-
- Phosphorus Research Bulletin
-
Phosphorus Research Bulletin 10 (0), 364-369, 1999
Japanese Association of Inorganic Phosphorus Chemistry
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205462797824
-
- NII論文ID
- 130004992354
-
- COI
- 1:CAS:528:DC%2BD3cXmtlOqtb8%3D
-
- ISSN
- 09184783
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可