Synthesis and Characterization of Highly Conductive PEDOT/PSS Colloidal Gels
-
- Horii Tatsuhiro
- University of Yamanashi
-
- Hikawa Hanae
- University of Yamanashi
-
- Mochizuki Yuta
- University of Yamanashi
-
- Okuzaki Hidenori
- University of Yamanashi
抄録
Poly(3,4-ethylenedioxythiophene) doped with poly(4-styrenesulfonate) (PEDOT/PSS) with various PSS composition ratios (α) was synthesized by oxidative polymerization and particle size distribution and zeta potential of the resulting colloidal gel particles were investigated by means of a dynamic light scattering technique. It was found that mean volume diameter of the PEDOT/PSS colloidal gel particles were 400-600 nm at α = 1~6, which drastically decreased to ~10 nm at α = 8~15. On the other hand, zeta potential was about -80 mV regardless of the composition ratio. The electrical conductivity of the PEDOT/PSS cast film measured by a four-point method attained as high as 263 S/cm at α = 3.
収録刊行物
-
- Transactions of the Materials Research Society of Japan
-
Transactions of the Materials Research Society of Japan 37 (4), 515-518, 2012
一般社団法人 日本MRS
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205513572096
-
- NII論文ID
- 130005004151
-
- COI
- 1:CAS:528:DC%2BC3sXjvFOjsLs%3D
-
- ISSN
- 21881650
- 13823469
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可