Evaluation of the Tensile Strength of Electron Beam Irradiated Powdered Ultra High Molecular Weight-Polyethylene (UHMWPE) Prior to Sintering
-
- Kanda Masae
- Department of Metallurgical Engineering, Graduate School of Engineering, Tokai University
-
- Deplancke Tiana
- MATEIS, UMR CNRS-INSA Lyon, Université de Lyon
-
- Lame Olivier
- MATEIS, UMR CNRS-INSA Lyon, Université de Lyon
-
- Nishi Yoshitake
- Department of Metallurgical Engineering, Graduate School of Engineering, Tokai University
-
- Cavaille Jean-Yves
- MATEIS, UMR CNRS-INSA Lyon, Université de Lyon
この論文をさがす
抄録
We have studied the variation in tensile strength (σb), fracture strain (εf) and Young modulus (dσ/dε) of low voltage electron beam irradiation (HLEBI) on powdered ultra-high molecular weight-polyethylene from 0.043 to 0.43 MGy prior to sintering. The low dose of 0.043 MGy-HLEBI enhanced the σb, εf and dσ/dε, as well as increased the crystallinity ratio from 37 to 46% evaluated by differential scanning calorimetry (DSC). An additional dose apparently decreased the σb and εf, as well as the melting point from approximately 412 to 406 K and the crystallinity ratio from 46 to 43% for 0.043 to 0.43 MGy, respectively. Irradiation induces two competitive mechanisms, namely (i) the scission of chains and (ii) the crosslinking of chains. The discussion is focused on these mechanisms.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (9), 1505-1508, 2015
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204253195392
-
- NII論文ID
- 130005094802
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026709632
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可