- Precipitation Behavior of Fine MX Type Carbide in Cr-Mo Steels
- Cr-Moコウ ニ オケル MXガタ ビサイ タンカブツ ノ セキシュツ キョドウ
この論文をさがす
抄録
This study deals with the influence of Ti addition on softening behavior of the martensite structure and precipitation behavior for 2 1/4Cr-1Mo-V steel. The fine MX type (Mo, V) C and (Mo, V, Ti ) C precipitate with heat treatment at from 600 to 700 deg. C after cooling from 1350 deg. C. These fine carbides coarse with the solute and precipitation of V, then the composition of carbides change to V-rich. (Mo, V, Ti) C in Ti-bearing steel keeps fine size even after long time heat treatment at high temperature. It is difficult to understand the retardation of coarsening of (Mo, V, Ti) C by Ostwald ripening theory. We therefore propose a hypothesis that (Mo, V, Ti) C is consequently maintained at fine size without coarsening by Ostwald ripening theory because the fine (Mo, V, Ti) C is practically insoluble due to very low solubility of Ti at heat treat temperature.
収録刊行物
-
- 材料
-
材料 64 (9), 732-738, 2015
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680420820736
-
- NII論文ID
- 130005098883
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 026757088
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可