In this study, we intended to increase the dimensionless figure of merit, ZT, of Al-Mn-Si based C54-phase using the precipitation of a small amount of Al-Mn-Si based C40-phase that possesses slightly smaller magnitude of both electrical resistivity and Seebeck coefficient. By knowing that both C54-phase and C40-phase in Al-Mn-Si alloy system are line compounds that are stabilized in a very narrow composition range, we prepared a series of samples by simply mixing two alloys consisting solely of C54-phase or C40-phase at [Al37(Mn26Ru3Re3Fe1)Si30]100−x[Al27.5(Mn29W3Fe1)Si39.5]x (x=0, 1, 3, 5, and 100). These initial alloys contained small amount of heavy elements for the reduction of lattice thermal conductivity. We found that the magnitude of Seebeck coefficient was kept essentially unchanged at x<3, while the lattice thermal conductivity and electrical resistivity were effectively decreased. The magnitude of ZT observed was increased by 16% from 0.38 of the single C54-phase at Al37(Mn26Ru3Re3Fe1)Si30 to ZT=0.42 at [Al37(Mn26Ru3Re3Fe1)Si30]97[Al27.5(Mn29W3Fe1)Si39.5]3.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 79 (11), 577-580, 2015
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458640896
-
- NII論文ID
- 130005105614
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 026843293
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可