CMAS damage in thermal barrier coatings: an exploration via single crystal bulk YSZ specimen
-
- HAYASHI Yuki
- Graduate School of Mechanical Engineering, Nagaoka University of Technology
-
- LOKACHARI Siddharth
- Graduate School of Mechanical Engineering, Nagaoka University of Technology
-
- YAMAGISHI Satoshi
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- OKAZAKI Masakazu
- Department of Mechanical Engineering, Nagaoka University of Technology
抄録
More recently a new type of damage has been pronounced in thermal barrier coatings (TBCs) by calcium-magnesium-alumino-silicates (CMAS) from ingestion of siliceous minerals under certain operating conditions. In order to understand material aspect of CMAS damage, a study on material interaction between molten CMAS and yttria-stabilized zirconia (YSZ) was carried out by using a single crystal YSZ material and a synthetic CMAS product in this work. Here the effect of crystallographic orientation on the interaction was also investigated. The CMAS-covered single crystal bulk YSZ specimens were isothermally exposed at high temperature. The experimental works clearly showed that interaction between the molten CMAS and YSZ was significant resulting in the change in microstructural morphology and composition of YSZ. The extent of interaction between CMAS and YSZ depended on the crystallographic plane of the YSZ: it was the lowest in the {111} crystallographic plane.
収録刊行物
-
- Mechanical Engineering Letters
-
Mechanical Engineering Letters 2 (0), 16-00240-16-00240, 2016
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680739427328
-
- NII論文ID
- 130005156298
-
- ISSN
- 21895236
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可