破壊機構再現法(ＦＲＡＳＴＡ)とその秘めたる可能性

DOI Web Site Web Site 被引用文献1件 参考文献10件

書誌事項

タイトル別名
  • Fracture Process Reconstruction Method (FRASTA) and Its Hidden Potential
  • ハカイ キコウ サイゲンポウ(FRASTA)ト ソノ ヒメタル カノウセイ

この論文をさがす

抄録

<p>Fracture surface topography analysis (FRASTA) technique reconstructs fracture process in microscopic details by matching conjugate fracture surface topographs. It produces three different results: fractured area projection plot (FAPP), cross-sectional plot (XSP), and fracture progression curve (FPC). FAPP shows graphically where the crack initiation site(s) is and how it grew. By superimposing a series of FAPPs over a scanning electron microscope image of fracture surface, we can establish relationships between fracture process and microstructures. XSP is used to characterize the crack tip opening displacement or crack opening angle. Use of these two results is seen in published papers where the crack initiation mechanisms could not be determined by regular fractographic examination. However, these two results do not indicate the kinematics of crack growth. FPC shows the relationship between fractured area and the spacing between conjugate surface topographs. This relatively unexplored relationship shows the crack growth history from the onset of microcrack initiation to the rupture of the component, and by analyzing this relationship such information as crack initiation time, crack growth rate, changes in loading conditions or environment can be learned. This paper presents some examples of use of FPC in failure analysis.</p>

収録刊行物

  • 材料

    材料 65 (11), 801-811, 2016

    公益社団法人 日本材料学会

被引用文献 (1)*注記

もっと見る

参考文献 (10)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ