OPTICAL FULL-FIELD INSPECTION METHOD OF STEEL FATIGUE CRACKING DUE TO THERMAL LOAD WITHOUT REMOVING COATING FILM
-
- MATSUDA Hiroshi
- 長崎大学 工学研究科
-
- KOGANEMARU Satoshi
- 長崎大学 工学研究科
-
- KUSANO Kazutoshi
- 元長崎大学 工学研究科
-
- ITO Yukihiro
- 佐賀大学 工学系研究科
-
- MORITA Chihiro
- 宮崎大学 工学研究科
Bibliographic Information
- Other Title
-
- 塗膜除去不要な鋼部材疲労亀裂の熱的負荷による光学的全視野探傷法
Abstract
In recent years, the occurrence case of fatigue crack has been an increase steel piers and steel deck, etc. in the road bridge. Depending on the site of the fatigue crack occurs, the crack is progress, cause brittle fracture. As a result, fatigue cracks will be a significant impact on the safety of the bridge. Therefore, finding them early, it is important to perform appropriate repair. This study is intended to develop a measurement method for detecting fatigue cracks. In this measurement method, first, by heating the steel members to open and close the cracks, and distortion difference before and after heating is measured using a digital image correlation method. This measurement method is a new detection method of crack defects of the steel member that does not require removal of the coating.
Journal
-
- Journal of Japan Society of Civil Engineers, Ser. A2 (Applied Mechanics (AM))
-
Journal of Japan Society of Civil Engineers, Ser. A2 (Applied Mechanics (AM)) 72 (2), I_643-I_652, 2016
Japan Society of Civil Engineers
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205351436672
-
- NII Article ID
- 130005311920
-
- ISSN
- 21854661
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed