- Basic Examination of Composite Magnetic Core with Surface-Oxidized Carbonyl-Iron Powder (CIP)/Epoxy for High <i>Q</i>-Factor RF-Inductor
抄録
<p> The carbonyl-iron powder (CIP) was annealed in the air for the composite core of high Q-factor RF-inductor to see if an oxidized film would be formed on CIP surface. Results showed that not only the surface-oxidized film thickness but also the crystallite diameter and coecivity increased when increasing the annealing temperature and time. The most suitable annealing conditions were found to be 240°C and 6 h: about 40 nm of Fe3O4 and Fe2O3 were formed on the CIP surface under these conditions. A magnetic composite with the surface-oxidized film on magnetic particles was fabricated and its permeability measured. The inductance and resistance were calculated by a 3D full-model electromagnetic analyzer on the basis of measured permeability and the Q-factor was then estimated using these characteristics. The highest Q-factor, 33, was observed at 1.8 GHz, which was higher than that of the air-core from 0.1 to 1.8 GHz.</p>
収録刊行物
-
- 日本磁気学会論文特集号
-
日本磁気学会論文特集号 1 (1), 34-39, 2017
公益社団法人 日本磁気学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205825937792
-
- NII論文ID
- 130005632301
-
- ISSN
- 24320471
-
- HANDLE
- 10091/00021260
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可