熱間押出法によるマグネシウム合金の超ジュラルミン被覆と表面特性の評価

DOI HANDLE Web Site Web Site 被引用文献1件 参考文献6件 オープンアクセス

書誌事項

タイトル別名
  • Coating on Magnesium Alloy with Super Duralumin by Hot Extrusion and Evaluation of Its Surface Properties
  • ネツカン オシダシホウ ニ ヨル マグネシウム ゴウキン ノ チョウジュラルミン ヒフク ト ヒョウメン トクセイ ノ ヒョウカ

この論文をさがす

抄録

<p>The poor corrosion resistance of Mg alloys, which is well known as one of the lightest structural metal materials, limits a wide use of these alloys. In order to dramatically increase not only the corrosion resistance but also the surface hardness of Mg alloys (AZ80), coating with A2024 Al alloy by hot extrusion has been attempted in this study. The coating was successfully realized by hot extrusion of a Mg alloy (AZ80) billet together with an Al alloy plate placed between the billet and the extrusion die. The A2024 Al alloy-coated Mg alloy exhibited an excellent corrosion resistance and no weight loss was observed after immersion in a 5 mass% HCl aqueous solution for 10 min while a weight loss of about 1500 g・m-2 was observed in case of AZ80 Mg alloy without coating under the same condition. The surface hardness of the coated alloy was increased to about 85 HV by aging for 144 h at room temperature after solution treatment for 3 h at 673 K.</p>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 81 (8), 389-393, 2017

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ