The effect of curing conditions on the dentin bond strength of two dual-cure resin cements
-
- Tagami Atsuko
- Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University (TMDU)
-
- Takahashi Rena
- Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University (TMDU)
-
- Nikaido Toru
- Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University (TMDU)
-
- Tagami Junji
- Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University (TMDU)
抄録
<p>Purpose: The purpose of this study was to determine the effect of the curing condition (i.e., the curing mode and restoration thickness) on the tensile bond strength of a dual-cure resin cement applied to dentin.</p><p>Methods: Indirect composite resin disks (1, 2, and 3mm in thickness) were prepared. The irradiance of a halogen light curing unit through each disk was measured by a curing radiometer. A measurement was also taken for the condition with no disk. Following this, two dual-cure resin cements, Panavia F2.0 and Panavia V5, were polymerized in either dualcure mode or self-cure mode to bond the composite resin disk to the flat dentin surface. The specimens were sectioned and subjected to a microtensile bond strength (μTBS) test after 24h of water storage. The data were statistically analyzed by two-way ANOVA followed with multiple comparisons by post-hoc Tukey's test (α=0.05).</p><p>Results: The irradiance values [mW/cm2] measured through indirect composite resin disks were 600 (0mm), 200 (1mm), 90 (2mm), and not detected (3mm). Two-way ANOVA indicated that both the curing condition and the type of resin cement affected the μTBS (p<0.001). The μTBS results for Panavia V5 bonded to dentin were significantly higher than those of Panavia F2.0 bonded to dentin (p<0.05).</p><p>Conclusions: The curing condition affected the tensile bond strength of the dual-cure resin cements to dentin. A newly developed resin cement, Panavia V5, showed higher dentin bonding than Panavia F2.0 in both dual- and self-cure modes.</p>
収録刊行物
-
- Journal of Prosthodontic Research
-
Journal of Prosthodontic Research 61 (4), 412-418, 2017
公益社団法人 日本補綴歯科学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205299958528
-
- NII論文ID
- 130006198540
-
- ISSN
- 18839207
- 18831958
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可