応力再分配効果が水素助長疲労き裂進展に及ぼす影響

書誌事項

タイトル別名
  • Influence of Stress Re-distribution on Hydrogen-induced Fatigue Crack Propagation
  • オウリョク サイブンパイ コウカ ガ スイソ ジョチョウ ヒロウ キレツ シンテン ニ オヨボス エイキョウ

この論文をさがす

抄録

<p>In order to clarify influence of stress re-distribution effect on hydrogen-induced fatigue crack propagation, we investigated fatigue crack propagation rates and brittle-like fracture ratio. The experiments were conducted in nitrogen and hydrogen gas atmosphere with ferrite-pearlite steels having different pearlite ratio, respectively. The crack propagation rates and the brittle-like fracture ratio decreased as pearlite ratio increased. To explain the changes of crack propagation rates and fracture ratio, we proposed that the stress re-distribution effect causing stress and strain relaxation at a crack tip contributes to suppression of the hydrogen-induced fatigue crack propagation. As a verification, finite element methods were operated with models having different width of the hard phase and different distance between a crack tip and a hard phase in plane stress and strain conditions, respectively. The finite element method analysis showed that stress re-distribution effect was smaller in plane strain condition than that in plane stress condition, indicating that a large hardness difference is crucial in plane stress condition to suppress the hydrogen-induced fatigue crack propagation.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 104 (1), 46-53, 2018

    一般社団法人 日本鉄鋼協会

参考文献 (25)*注記

もっと見る

詳細情報

問題の指摘

ページトップへ