Fatigue Behavior of Fe-Cr-Ni-based Metastable Austenitic Steels with an Identical Tensile Strength and Different Solute Carbon Contents
-
- Ogawa Takuro
- Department of Mechanical Engineering, Kyushu University
-
- Koyama Motomichi
- Department of Mechanical Engineering, Kyushu University
-
- Nishikura Yuri
- Department of Mechanical Engineering, Kyushu University
-
- Tsuzaki Kaneaki
- Department of Mechanical Engineering, Kyushu University
-
- Noguchi Hiroshi
- Department of Mechanical Engineering, Kyushu University
Bibliographic Information
- Other Title
-
- 同引張強度かつ異なる固溶炭素量を有するFe-Cr-Ni基準安定オーステナイトステンレス鋼の疲労挙動
- ドウ ヒッパリ キョウド カツ コトナル コヨウ タンソリョウ オ ユウスル Fe-Cr-Ni キジュン アンテイ オーステナイトステンレスコウ ノ ヒロウ キョドウ
- Fatigue behavior of Fe-Cr-Ni-based metastable austenitic steels with an identical tensile strength and different solute carbon contens
Search this article
Abstract
<p>Fatigue properties of Fe-19Cr-8Ni-0.05C and Fe-19Cr-8Ni-0.14C steels were investigated using a rotating bending fatigue test machine. Fatigue limit of both of the steels were dominated by critical stress amplitude for crack initiation. Because of the austenite stability, the fatigue limit of the Fe-19Cr-8Ni-0.05C steel was 200 MPa higher than that of the Fe-19Cr-8Ni-0.14C steel. Although occurrence of dynamic strain aging in the Fe-19Cr-8Ni-0.14C was expected to improve fatigue limit, the effect did not appear due to the remarkable increase of phase stability that deteriorates positive effects of transformation-induced plasticity and transformation-induced crack closure.</p>
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 104 (2), 88-97, 2018
The Iron and Steel Institute of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680194269184
-
- NII Article ID
- 130006325925
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 028821421
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed