書誌事項
- タイトル別名
-
- Geometrical Evaluation of Inclusions in Cast Aluminum Alloy by Using Synchrotron Radiation Microtomography and Its Contribution to Fatigue Crack Initiation
抄録
<p>Cast aluminum alloys have been widely used in transportation equipment because of its high productivity and high specific strength. However, the cast aluminum alloys have low reliability of fatigue strength caused from inevitable casting defect. In our previous work, from the low cycle fatigue test and in situ synchrotron X-ray CT observation of the cast aluminum alloy, it was found that the crack initiation of the cast aluminum alloy was occurred by the fracture of Si particles. In this study, the fracture of Si particle was regarded as the crack initiation, and the geometrical characteristic of fractured Si particle was investigated. The fractured and intact Si particles were identified by chronological CT observation. Geometrical analyses of Si particles were conducted by using high resolution CT images, while Si particles were extracted by an appropriate threshold value of brightness. Geometrical parameters of a few hundreds of thousand Si particles in a specimen were analyzed, then they were evaluated statistically. The effective geometrical parameters were suggested to determine the condition of particle fracture.</p>
収録刊行物
-
- 年次大会
-
年次大会 2017 (0), G0300405-, 2017
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680819785088
-
- NII論文ID
- 130006549907
-
- ISSN
- 24242667
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可