- Effects of Processing Parameters on Tensile Shear Strength of Woven CF/PPS Laminates joined by Electro Fusion Welding
抄録
<p>This study aims to develop the resistance welding method for continuous fiber reinforced thermoplastic (cFRTP) composites using Woven-CF 0/90° as resistance heating element. The material for the experiment was woven CF/PPS laminates. The effects of processing conditions such as applied current, time and pressure, and also material conditions such as thickness of the inserted PPS films on the fusion behavior of cFRTP composites were investigated to get the optimum condition for electro-fusion joining. The contents for evaluation were surface condition of joint section peeled off after applying current and welding area obtained from those images. The experimental results revealed that electro-fusion behavior was influenced significantly by thickness of PPS films and electric resistivity of cFRTP laminates. From the result of the single lap shear strength (LSS) test, it was revealed that the LSS value of using Woven-CF 0/90° heating element was achieved over 24MPa.</p>
収録刊行物
-
- 年次大会
-
年次大会 2017 (0), J0440204-, 2017
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205843246720
-
- NII論文ID
- 130006550265
-
- ISSN
- 24242667
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可