Growth of transparent SrB<sub>4</sub>O<sub>7</sub> crystal fiber by the μ-PD method
-
- Machida Takaaki
- Graduate School of Sciences and Technology for Innovation, Yamaguchi University
-
- Inaba Sho
- Graduate School of Sciences and Technology for Innovation, Yamaguchi University
-
- Ueda Maki
- Graduate School of Sciences and Technology for Innovation, Yamaguchi University
-
- Asakawa Harutoshi
- Graduate School of Sciences and Technology for Innovation, Yamaguchi University
-
- Komatsu Ryuichi
- Graduate School of Sciences and Technology for Innovation, Yamaguchi University
抄録
<p> We grew transparent SrB4O7 (SBO) crystal fibers by the micro-pulling-down (μ-PD) method at pulling rates (VP) of 0.01–0.40 mm/min. We observed the SBO crystals by optical microscopy. The SBO crystal fiber at VP of 0.40 mm/min was cloudy due to the incorporation of voids. In contrast, transparent single-crystal fibers were obtained at VP of less than 0.02 mm/min. This is the first time that transparent SBO crystal fibers have been grown with a length of several centimeters. These results demonstrate that it is crucial to grow SBO crystals at a low VP to obtain transparent crystal fibers. In addition, we considered the generation mechanism of voids in the SBO crystals by using the relation between the growth rate of SBO crystals and the diffusion rate of voids.</p>
収録刊行物
-
- Transactions of the Materials Research Society of Japan
-
Transactions of the Materials Research Society of Japan 42 (3), 65-68, 2017
一般社団法人 日本MRS
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680489920640
-
- NII論文ID
- 130006943321
-
- ISSN
- 21881650
- 13823469
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可