Influence on Wood Color of Relative Humidity in Conditioning Process of Dye-Aqueous Solution Impregnated Wood
-
- TANAKA Soichi
- Res. Inst. for Sustainable Humanosphere
-
- SUGINO Hideaki
- Res. Inst. for Sustainable Humanosphere Gisen Co., Ltd.
-
- SEKI Masako
- Structural Materials Res. Inst., Advanced Industrial Sci. and Tech. (AIST)
-
- MIKI Tsunehisa
- Structural Materials Res. Inst., Advanced Industrial Sci. and Tech. (AIST)
-
- UMEMURA Kenji
- Res. Inst. for Sustainable Humanosphere
-
- KANAYAMA Kozo
- Res. Inst. for Sustainable Humanosphere
Bibliographic Information
- Other Title
-
- 染料水溶液含浸木材の養生過程における相対湿度が材色に及ぼす影響
- センリョウ スイヨウエキ ガンシン モクザイ ノ ヨウジョウ カテイ ニ オケル ソウタイ シツド ガ ザイショク ニ オヨボス エイキョウ
Search this article
Abstract
<p>The purpose of our study was to clarify the influence on wood color of relative humidity (RH) in conditioning, or process of evaporating water, of dye-aqueous solution impregnated wood. The cross-cut (RT) or quarter-sawn (LR) sample of hinoki (Chamaecyparis obtusa) was impregnated with a 0.1 mass% aqueous solution of patent blue VF (PB), and subsequently conditioned at several levels of RHs (40 °C) to reach to a constant mass. The conditioned samples were dried at 40 °C over phosphorus pentoxide in a vacuum and observed by microscope, and each parameters of the sample in L*a*b* color space were measured by color spectrometer. With the increase in RH, the values of L* and b* for the RT and LT surfaces of the RT and LT samples, respectively, increased and became closer to those for the untreated samples. This was considered to be caused by the decrease in the amount of PB on the surface of cell walls with increasing RH because of the increase in the diffusivity of PB into cell walls. In the RT cross section of LR sample, the area of the deeper color was concentrated into the center of the cross-section if the RH was high, which indicates the macroscopic diffusion of PB from the surface to the center in the sample.</p>
Journal
-
- Journal of the Society of Materials Science, Japan
-
Journal of the Society of Materials Science, Japan 67 (8), 767-772, 2018-08-15
The Society of Materials Science, Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390564238010273152
-
- NII Article ID
- 130007437250
-
- NII Book ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL BIB ID
- 029208298
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed