Micro-Vickers Hardness of Intermetallic Compounds in the Zn-rich Portion of Zn–Fe Binary System
-
- Han Kwangsik
- Department of Materials Science, Tohoku University
-
- Lee Inho
- Department of Materials Science, Tohoku University
-
- Ohnuma Ikuo
- Computational Materials Science Unit, National Institute for Materials Science (NIMS)
-
- Okuda Kaneharu
- Steel Research Laboratory, JFE Steel Corporation
-
- Kainuma Ryosuke
- Department of Materials Science, Tohoku University
Abstract
<p>Annealing temperature and composition dependences of hardness for the intermetallic compound phases, especially Γ-Fe4Zn9, δ1p-Fe13Zn126 and δ1k-FeZn7, which are obtained in Zn-rich portion of Fe–Zn alloys, were investigated by the micro-Vickers hardness test. Although the hardness of the Γ and δ1k phases only slightly decreases with increasing quenching temperature, it shows obvious composition dependences. However, the hardness of the disordered δ1p phase is basically lower than that of the ordered δ1k phase, which is hardly affected by composition change. The hardness of all the Zn-rich compound phases quenched from 500°C (or 550°C) are evaluated and compared.</p>
Journal
-
- ISIJ International
-
ISIJ International 58 (9), 1578-1583, 2018-09-15
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390845713001414016
-
- NII Article ID
- 130007484967
-
- ISSN
- 13475460
- 09151559
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed