Sorption capacity of Cs+ on titania nanotubes synthesized by solution processing
-
- GOTO Tomoyo
- The Institute of Scientific and Industrial Research (ISIR), Osaka University
-
- CHO Sung Hun
- The Institute of Scientific and Industrial Research (ISIR), Osaka University
-
- LEE Soo Wohn
- Department of Environmental and Bio-Chemical Engineering, Sun Moon University
-
- SEKINO Tohru
- The Institute of Scientific and Industrial Research (ISIR), Osaka University
書誌事項
- タイトル別名
-
- Sorption capacity of Cs<sup>+</sup> on titania nanotubes synthesized by solution processing
抄録
<p>Titania nanotubes (TNTs) have nanometer-sized tubular morphologies with layered structures. TNTs are candidate sorbents for the removal of many heavy metals and radionuclides. In this study, we investigated the Cs+ sorption capacity of TNTs synthesized by a solution chemical method in comparison with those of zeolite and TiO2 particles. The TNT powder was shaken in 0.2–4.0 mM CsCl aqueous solution at 10, 25, and 40°C for up to 7 days. The sorption tests showed that the sorption density of Cs+ per gram of TNT was lower than that of zeolite. TiO2 did not show Cs+ adsorption. The sorption isotherm of Cs+ on TNTs was fitted with the Langmuir model. The sorption of Cs+ on zeolite was well described with the Freundlich model. The TNT structure was maintained after sorption testing regardless of the concentration of CsCl aqueous solution. Elemental analysis of the TNTs showed uniformly adsorbed Cs+ throughout the TNTs. Na+ was also detected in the TNTs both before and after sorption, but the residual Na+ concentration decreased with increasing the adsorbed Cs+ concentration. These results clearly showed that the Cs+ was intercalated into the layered structures of the TNTs by ion-exchange with Na+.</p>
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 126 (10), 801-807, 2018-10-01
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282763050379264
-
- NII論文ID
- 130007493316
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可