Investigation of the Cross-Sectional Structure and Isothermal Section at 1150°C of a Nb-Re-Si Alloy Fabricated Using a Tetra-Arc Furnace
-
- Saito Shigeru
- Laboratory of Advanced Materials for Cold Region, Hokkaido University of Science
-
- Takashima Toshiyuki
- Hokkaido University of Science
-
- Horiuchi Toshiaki
- Laboratory of Advanced Materials for Cold Region, Hokkaido University of Science
-
- Miura Seiji
- Faculty of Engineering, Hokkaido University
-
- Narita Toshio
- DBC System R&D Co., Ltd.
Bibliographic Information
- Other Title
-
- テトラアーク引上炉を用いて作製したNb-Re-Si合金の断面組織と1150°Cにおける等温断面図の検討
- テトラアーク ヒキアゲロ オ モチイテ サクセイ シタ Nb-Re-Si ゴウキン ノ ダンメン ソシキ ト 1150℃ ニ オケル トウオン ダンメンズ ノ ケントウ
Search this article
Abstract
<p>Ternary Nb-Re-Si alloy samples were melted and pulled simultaneously in a tetra-arc furnace and rapidly water-quenched after heat treatment at 1150°C for 1200 h. The microstructures of the samples that had been water-quenched after heat treatment were observed and the Nb, Re and Si concentrations in the constituent phases were measured using an electron probe microanalyzer (EPMA). In the cross-sectional structure of the obtained alloy samples, the lower portion of the pulled part consists of Nb5Si3 and Nb-Re-Si ternary compound phases. By contrast, the upper portion consists of Nb5Si3 and Nb solid solution phases. The Nb solid-solution phase, Nb5Si3 and Nb-Re-Si ternary compound are in equilibrium. It was found that the solubility limit of Si in the Nb solid-solution phase ranges from 0.6 to 1.7 at%, while the solubility limit of Re in the Nb5Si3 phase is 1.3-2.0 at%. The maximum amount of Re in the Nb5Si3 phase in equilibrium with the Nb solid solution is about 0.9 at%.</p>
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 82 (11), 409-414, 2018-11-01
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390845713013686400
-
- NII Article ID
- 130007500793
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 029333017
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed