- Site Occupation State of Deuterium Atoms in fcc Fe
- サイエンス記事 fcc Fe中の重水素原子のサイト占有状態
- サイエンス キジ fcc Fe チュウ ノ ジュウスイソ ゲンシ ノ サイト センユウ ジョウタイ
この論文をさがす
抄録
<p>The deuterization process of fcc Fe to form solid‒solution fcc FeDx was investigated by in situ neutron diffraction measurements at high temperature and high pressure. In a completely deuterized specimen at 988 K and 6.3 GPa, deuterium atoms occupy the octahedral and tetrahedral interstitial sites with an occupancy of 0.532(9) and 0.056(5), respectively, giving a deuterium composition x of 0.64(1). During deuterization, the metal‒lattice expands approximately linearly with deuterium composition at a rate of 2.21 Å3 per deuterium atom. The minor occupation of tetrahedral site is likely driven by the intersite movement of deuterium atoms along the <111> direction in the fcc metal lattice. These results provide implications for the light elements in the Earth's core and the mechanism of hydrogen embrittlement of ferrous metals.</p>
収録刊行物
-
- 波紋
-
波紋 25 (1), 26-31, 2015
日本中性子科学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001288091203328
-
- NII論文ID
- 130007510577
-
- NII書誌ID
- AA11905115
-
- ISSN
- 1884636X
- 1349046X
-
- NDL書誌ID
- 026095271
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可