- Fatigue Limit Improvement and Rendering a Defect Harmless for Stainless Steel Welded Joint Containing a Crack-like Surface Defect
- き裂状表面欠陥を有するステンレス鋼溶接継手の疲労限度改善と欠陥の無害化 : レーザピーニングの効果
- キレツジョウ ヒョウメン ケッカン オ ユウスル ステンレスコウ ヨウセツ ツギテ ノ ヒロウ ゲンド カイゼン ト ケッカン ノ ムガイカ : レーザピーニング ノ コウカ
- -Effects of Laser Peening-
- -レーザピーニングの効果-
この論文をさがす
抄録
The effects of laser peening (LP) on the bending fatigue limit of an austenitic stainless steel JIS-SUS316 welded joint containing an artificial semi-circular slit on the weld toe were investigated. The optimum LP condition which was expected to have a good effect in fatigue limit improvement was determined by measuring the residual stress distributions for several LP conditions. Then, three-point bending fatigue tests were carried out at a stress ratio of R=0.05 for both LP treated welded specimens with the slit on the weld toe and those without the slit. The fatigue limits of all specimens increased by 23-64% due to LP. LP treated specimens with a slit depth of a=0.2 mm had high fatigue limits that were nearly equal to those of non-slit, LP treated specimens. Therefore, a semi-circular slit of less than a=0. 2 mm could be rendered harmless due to LP. The improvement of fatigue limit due to LP was mainly achieved by compressive residual stress.
収録刊行物
-
- 圧力技術
-
圧力技術 57 (2), 82-91, 2019
一般社団法人 日本高圧力技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282763110926592
-
- NII論文ID
- 130007636820
-
- NII書誌ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL書誌ID
- 029627869
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可