High-Temperature Thermoelectric Properties of Pr<sub>1−</sub><i><sub>x</sub></i>Sr<i><sub>x</sub></i>FeO<sub>3</sub> (0.1 ≤ <i>x</i> ≤ 0.7)
-
- Nakatsugawa Hiroshi
- Yokohama National University
-
- Saito Miwa
- Kanagawa University
-
- Okamoto Yoichi
- National Defense Academy
Bibliographic Information
- Other Title
-
- High-Temperature Thermoelectric Properties of Pr[1-x]Sr[x]FeO₃ (0.1 ≤ x ≤ 0.7)
Search this article
Abstract
<p>Polycrystalline specimens of Pr1−xSrxFeO3 (0.1 ≤ x ≤ 0.7) were synthesized using a solid state reaction method. All samples had a typical perovskite structure, where the orthorhombic (Pbnm) phase was dominant at x ≤ 0.5 and the rhombohedral (R-3c) phase was dominant at x ≥ 0.6. Since the B site is in the mixed valence state of Fe3+/Fe4+ and the spin quantum number is in the range of 0.86 ≤ s ≤ 1.15, it is expected that Fe3+ is in the spin state of low spin (LS) Fe3+ or intermediate spin (IS) Fe3+ and Fe4+ is in the spin state of LS Fe4+. As x increases, the ratio of IS Fe3+ decreases compared to that of LS Fe3+ at x ≥ 0.3, so that the P-type Seebeck coefficient is maintained up to x = 0.5. Although ZT = 0.002 (T = 850 K) of x = 0.7 which shows the maximum N-type thermoelectric characteristic is about 8% of ZT = 0.024 (T = 850 K) of x = 0.1 which shows the maximum P-type thermoelectric characteristic, both are the results of relatively high Seebeck coefficient, low electrical resistivity, and low thermal conductivity. Therefore, we strongly suggest that there is a possibility of application of PN elements which compose of the perovskite-type oxides.</p><p> </p><p>This Paper was Originally Published in Japanese in J. Thermoelec. Soc. Jpn. 15 (2018) 3–13.</p>
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 60 (6), 1051-1060, 2019-06-01
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001288140681472
-
- NII Article ID
- 40021904726
- 130007653138
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 029707477
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed