Micro-Photoelastic Evaluation of Indentation-Induced Stress in Glass
-
- Asai Keisuke
- The University of Shiga Prefecture
-
- Yoshida Satoshi
- The University of Shiga Prefecture
-
- Yamada Akihiro
- The University of Shiga Prefecture
-
- Matsuoka Jun
- The University of Shiga Prefecture
-
- Errapart Andrei
- Trenz Electronic GmbH
-
- Kurkjian Charles R.
- Rutgers University
この論文をさがす
抄録
<p>In this study, micro-photoelastic measurements were performed to obtain three-dimensional stress maps of silica and soda-lime glasses during ball indentation. The stress components were calculated from retardations and azimuths, which were determined from photoelastic measurements with a spatial resolution of about 1 µm. During loading, it was observed that the tensile stress in the radial direction is generated near the surfaces of both glasses. During unloading, however, it was found that stress distributions of silica and soda-lime glasses are different from each other. It is concluded that the different stress distributions during indentation result in different crack geometries, ring and radial cracks.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 60 (8), 1423-1427, 2019-07-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001288154777600
-
- NII論文ID
- 130007683559
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 029819135
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可