Poly(3,4-ethylenedioxythiophene) Grains Synthesized by Solvent-free Chemical Oxidative Polymerization
-
- Hiroki Inoue
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Natsuko Shimogama
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Musashi Seike
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Keigo Oyama
- Division of Applied Chemistry, Graduate School of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Shun Mukai
- Division of Applied Chemistry, Graduate School of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Shinya Higashimoto
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Tomoyasu Hirai
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Yoshinobu Nakamura
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
-
- Syuji Fujii
- Department of Applied Chemistry, Faculty of Engineering, Osaka Institute of Technology, 5-16-1 Omiya, Asahi-ku, Osaka 535-8585 , Japan
抄録
<jats:title>Abstract</jats:title> <jats:p>Poly(3,4-ethylenedioxythiophene) (PEDOT) grains were synthesized by solvent-free chemical oxidative polymerization in one-step and one-pot manner. The resulting PEDOT grains had atypical shapes with a volume-average diameter of 57 ± 45 µm and showed an electrical conductivity of 1.9 × 10−3 S cm−1. Furthermore, it was clarified that the PEDOT grains showed light-to-heat photothermal property.</jats:p>
収録刊行物
-
- Chemistry Letters
-
Chemistry Letters 48 (8), 968-970, 2019-06-04
Oxford University Press (OUP)
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1360283694082782208
-
- NII論文ID
- 130007687702
-
- ISSN
- 13480715
- 03667022
-
- データソース種別
-
- Crossref
- CiNii Articles
- KAKEN