極厚鋼板およびその溶接継手部の小型引張試験片による破壊靭性値評価に関する一考察

DOI Web Site

書誌事項

タイトル別名
  • A Study on Fracture Toughness of Heavy-Thick-Steel Plates and Its Welded Joints by Small Size Tension Test Specimen
  • ゴクアツ コウハン オヨビ ソノ ヨウセツ ツギテブ ノ コガタ ヒッパリ シケンヘン ニ ヨル ハカイジンセイチ ヒョウカ ニ カンスル イチ コウサツ

この論文をさがす

抄録

It is needed to obtain the fracture toughness of butt-welded joints of heavy thick steel plates accurately to ensure strength and reliability of upper structure of very large container ships using heavy thick steel plate with 50 to 100mm thickness.<br>In our previous study, the tensile test by using the center notched small size tension test specimen had been proposed to obtain the fracture toughness KIC for unstable brittle fracture initiated at the tip of a fatigue crack which generates on the surface of butt-welded joint of heavy thick high-tensile strength steel plates then propagates from there.<br>In this study, the fracture toughness KIC values of butt-welded joints of heavy thick high-tensile strength steel plates (YP36, YP40, YP47) for ship building by the center notched small size tension tests were evaluated. As the results, by using the center notched small size tension test specimen, valid fracture toughness KIC can be obtained and by adding the effect of the weld residual stress the fracture toughness KIC values of the welded joints by the center notched small size tension tests show good agreement to them by the center notched wide plate tension tests.

収録刊行物

  • 圧力技術

    圧力技術 57 (4), 201-211, 2019

    一般社団法人 日本高圧力技術協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ