- Fatigue Strength Evaluation of Spheroidal Graphite Cast Iron with Small Defects on Casting Surface and Machined Surface
- キュウジョウ コクエン チュウテツ ノ チュウハダ オヨビ カコウハダ ノ ビショウ ケッカン ト ヒロウ トクセイ ヒョウカ
この論文をさがす
抄録
<p> In most spheroidal graphite cast iron, tiny casting defects such as abnormal graphite, micro shrinkage, and inclusions, etc. occur near the casting surface. These defects deteriorate the fatigue strength depending on the size and distribution. Since the defects size is mostly within a range of 100 to 1000 μm, it is difficult to detect them in the production process. In this study, ferritic-pearlitic spheroidal graphite cast iron specimens were prepared with casting surface and machined surface. Then, a simple measurement of the defects size was carried out by microstructure observation or low temperature fracture testing. The estimated value of the maximum defect size could successfully be evaluated based on the statistics of extremes analysis for both micro shrinkage and dross defect near the casting surface. Moreover, four-point bending fatigue tests were performed at an R of 0.3 to investigate the influence of the defects near the casting surface on the fatigue strength. The S-N data showed a scatter because of the influences of the different defect sizes in respective specimens. The influence of the defects on the fatigue limit could be predicted by both statistics of extremes analysis of the defect size and the √areamax parameter model. Several examples will be also given on how to apply these methods for designing ductile cast iron products.</p>
収録刊行物
-
- 鋳造工学
-
鋳造工学 91 (12), 869-875, 2019-12-25
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390283659837147648
-
- NII論文ID
- 130007778809
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 030148149
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可