Fabrication and Enhanced Vickers Hardness of Electrodeposited Co–Cu Alloy Film with High Composition Gradient
-
- Hagiwara Hiroyuki
- Department of Mechanical Engineering, Osaka City University
-
- Kaneko Yoshihisa
- Department of Mechanical Engineering, Osaka City University
-
- Uchida Makoto
- Department of Mechanical Engineering, Osaka City University
この論文をさがす
抄録
<p>By applying an oscillating potential wave, we obtained an electrodeposited Co–Cu alloy film in which the Co concentration changed periodically at a short modulation wave length. A triangular Co concentration modulation was observed along the film growth direction. The local composition gradient became as high as 50 at%/µm. The Vickers hardness of the composition gradient film was 380 HV. Because this value was much higher than that of simple electrodeposited Co–Cu alloy films, contribution of the composition-gradient structure to hardness was suggested.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 61 (4), 801-804, 2020-04-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390002184886696576
-
- NII論文ID
- 130007815407
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 030344905
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可