Formation of LPSO Phases in As-Cast Mg–Al–Zn–Gd Quaternary Alloys

• Masaoka Kazuki

  Hokkaido University of Science

• Yamada Tadayuki

  Hokkaido University of Science

• Horiuchi Toshiaki

  Laboratory of Advanced Materials for Cold Region (LAM), Hokkaido University of Science

• Itoi Takaomi

  Faculty of Engineering, Chiba University

• Miura Seiji

  Faculty of Engineering, Hokkaido University

Abstract

Mg alloys with a long-period stacking-order (LPSO) phase are categorized into two types. Those in which the LPSO phase forms in as-cast state are referred to as Type I, while those in which the LPSO phase does not appear until a heat treatment is performed are categorized as Type II. However, the reason that gives rise to these two types of alloy is still not well understood. In the present study, in an attempt to clarify this issue, three different Mg₈₅(Al,Zn)₆Gd₉ quaternary alloys were prepared. The α-Mg, Al₂Gd, Mg₃Gd and LPSO phases were identified in the as-cast quaternary alloys by microstructural observations, composition analysis and crystal structure analysis using electron probe microanalysis and X-ray diffraction. The results indicated that all the quaternary alloys could be categorized as Type I, even though ternary Mg₈₅Al₆Gd₉ and Mg₈₅Zn₆Gd₉ alloys were Type II. The crystal structure of the LPSO phase in the as-cast alloys is considered to be18R with dilute solute elements, and the fraction of this phase increases with increasing Zn content. The presence of this phase is thought to be the cause of destabilization of the primary Al₂Gd phase. It is thus concluded that the relative stability of phases in the vicinity of the LPSO phase is crucial in determining the type of Mg alloy formed.   This Paper was Originally Published in Japanese in J. Japan Inst. Met. Mater. 83 (2019) 257–263.

Journal

• MATERIALS TRANSACTIONS

  MATERIALS TRANSACTIONS 61 (5), 849-855, 2020-04-01

  The Japan Institute of Metals and Materials

Keywords

• magnesium alloy
• long period stacking order
• magnesium–aluminum–zinc–gadolinium quaternary alloy
• formation type

Details

• CRID: 1390848250106605696
• NII Article ID: 130007835704
• NII Book ID: AA1151294X
• DOI: 10.2320/matertrans.mt-mm2019008
• ISSN: 13475320
• ISSN: 13459678
• NDL BIB ID: 030380919
• Web Site: http://id.ndl.go.jp/bib/030380919
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I030380919
• Web Site: https://www.jstage.jst.go.jp/article/matertrans/61/5/61_MT-MM2019008/_pdf
• Text Lang: en
• Data Source:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
  • KAKEN
• Abstract License Flag: Disallowed