- Evaluation of Durability of SCM435 Steel for High-pressure Hydrogen System by Continuous Cathodic Hydrogen Charging SSRT
- (Effects of Hydrogen Charging Method)
- (水素チャージ方法の影響)
抄録
<p>As an alternative method to evaluation of slow strain rate technique (SSRT) under high-pressure hydrogen gas, Continuous Cathodic Hydrogen Charging SSRT tests were performed. Cr-Mo low alloy steel with a tensile strength of 1000 MPa grade was selected as a test material. Cathodic charging was performed in 3% NaCl aqueous solution at a current density of 400 A/m2 and 1N-NaOH aqueous solution at 1.354 V constant potential test. Relative reduction of area (RRA) values obtained by tests with continuous charge at a cathode were equivalent to those performed in hydrogen gas at pressure of 69 ~ 115 MPa. The amount of hydrogen was measured using TDA. Amount of diffusible hydrogen is 0.74 ~1.09 ppm, which is equivalent to using hydrogen gas with a pressure of 69 ~ 115 MPa. Fracture surface observations were performed using scanning electron microscopy (SEM). The quasi-cleavage fracture surface of hydrogen embrittlement (QCHE) was observed near the surface of specimen that were subjected to continuously hydrogen charged tests.</p>
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2019 (0), OS0613-, 2019
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390566775136093312
-
- NII論文ID
- 130007846454
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可