Low-temperature degradation of high-strength Y-TZP (yttria-stabilized tetragonal zirconia polycrystal)
-
- FURUYA Katsunori
- Department of Removable Partial Prosthodontics, Tokyo Dental College
-
- TAKEMOTO Shinji
- Department of Biomedical Engineering, Iwate Medical University
-
- YAMASHITA Shuichiro
- Department of Removable Partial Prosthodontics, Tokyo Dental College
-
- SEKINE Hideshi
- Department of Prosthetic Dentistry, School of Dentistry, Ohu University
-
- YAJIMA Yasutomo
- Department of Oral and Maxillofacial Implantology, Tokyo Dental College
-
- YOSHINARI Masao
- Oral Health Science Center, Tokyo Dental College
この論文をさがす
抄録
<p>The objective of this study was to investigate the low temperature degradation characteristics of 2 types of high strength yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) in order to evaluate its suitability for implant body, implant superstructure or abutment. Disk-shaped conventional Y-TZP (0.25 mass% alumina) subjected to hot isostatic press treatment (HIP-Y-TZP) and Y-TZP/4Al2O3 with additional alumina (4.0 mass%) were mirror-polished. Accelerated aging tests with 134°C for 5 h at 0.2 MPa and 180°C for 5 h at 1.0 MPa were performed using an autoclave. Biaxial flexural strength and crystal phases were evaluated. Strength decreased as the proportion of monoclinic phase increased after accelerated aging treatment for both types of high-strength Y-TZPs. Despite the low alumina content, HIP-Y-TZP showed higher static strength and strength after accelerated aging treatment compared to Y-TZP/4Al2O3. However, both types of Y-TZP had adequate strength to be used as dental restorations even after accelerated aging treatment, therefore, its clinical suitability was considered high.</p>
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 39 (4), 577-586, 2020-07-30
日本歯科理工学会