Effect of Formic Acid on Corrosion Behavior of STBA24 Low-Alloyed Steel and Its Weldment in Simulated Boiler Water Containing Chloride Ions
-
- Niu Li-Bin
- Institute of Engineering, Academic Assembly, Shinshu University
-
- Kosaka Shoichi
- Institute of Engineering, Academic Assembly, Shinshu University
-
- Yoshida Masaki
- Naigai Chemical Products Co., Ltd.
-
- Suetake Yusuke
- Naigai Chemical Products Co., Ltd.
-
- Marugame Kazuo
- Naigai Chemical Products Co., Ltd.
この論文をさがす
抄録
<p>The effect of formic acid (HCOOH) in simulated boiler water containing chloride ions (Cl−) on the corrosion behavior of STBA24 low-alloyed steel and its weldment was investigated using electrochemical corrosion tests, immersion corrosion tests and surface analyses. The addition of 100 ppm HCOOH into water containing 100 ppm Cl− resulted in thicker films with poor corrosion resistance that were formed easily on both the base metal and the weldment of STBA24, even though pit initiation was inhibited within a short time. The results suggest that the presence of 100 ppm formic acid in the simulated boiler water containing 100 ppm chloride ions promotes corrosion of the materials tested.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 61 (9), 1775-1781, 2020-09-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390566775160827008
-
- NII論文ID
- 130007890395
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 030599744
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可