- Improvement of Reliability of Fatigue Properties of High Strength Steel Applying Surface Crack Non-damaging Technology
- ヒョウメン キレツ ムガイカ ギジュツ ノ オウヨウ ニ ヨル ヒロウ ゲンド セッケイ サレタ コウキョウドコウ ノ シンライ セイコウ ジョウ
この論文をさがす
抄録
Recently, a technique has been developed to render harmless surface cracks which reduce the fatigue limit of metals by 20~60% by the effects of compres-sive residual stress induced by shot peening. This technique is called as sur-face crack non-damaging technology. For the purpose of contributing to reliability improvement of high strength steel equipment by surface crack non-damaging technology, the following research was carried out:<br>(a) The effects of aspect ratio of surface crack on maximum harmless crack depth (ahlm) of a high strength was calculated for three residual stress distributions. <br>(b) Assuming the value of safety factor, the relationship between the maximum allowable crack depth (acrN) and ahlm was investigated. <br>(c) The relationship between maximum detectable crack depth by non-destructive inspection (aNDI) and ahlm was compared, assuming that nondestructive inspection could detect the crack with sufficient probability. <br>(d) The relationship between ahlm, aNDI and ahlm were compared.
収録刊行物
-
- 圧力技術
-
圧力技術 58 (5), 263-271, 2020
一般社団法人 日本高圧力技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1391975276375034880
-
- NII論文ID
- 130007931409
-
- NII書誌ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL書誌ID
- 030695106
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可