Synthesis, photoluminescence, and up-conversion luminescence of niobates co-doped with Er<sup>3+</sup> and Yb<sup>3+</sup>
-
- HIRANO Masanori
- Department of Applied Chemistry, Faculty of Engineering, Aichi Institute of Technology
-
- IWATA Hiroyuki
- Department of Electrical and Electronics Engineering, Faculty of Engineering, Aichi Institute of Technology
-
- TANAKA Kouki
- Department of Applied Chemistry, Faculty of Engineering, Aichi Institute of Technology
抄録
<p>Niobates, CaNb2O6 with columbite-type structure doped with Er3+ (CaNb2O6:Er3+) and co-doped with Er3+ and Yb3+ (CaNb2O6:Er3+/Yb3+) were synthesized from precursor solutions using inorganic salts under mild hydrothermal conditions at 240 °C. The as-prepared niobates appeared to be a sheaf of aligned acicular particles. At 3 mol % Er3+, the as-prepared CaNb2O6:Er3+ showed the strongest photoluminescence (PL) in the characteristic green spectral region corresponding to the 2H11/2 → 4I15/2 and 4S3/2 → 4I15/2 transitions of Er3+. The green PL intensity of the sample doped with 5 mol % Er3+ after heating at 1300 °C in air was more than 10 times stronger than that before heating when exciting directly at 377 nm. The effect of the concentration of the sensitizer Yb3+ on the up-conversion emission of CaNb2O6:Er3+/Yb3+ was investigated using samples after heating in air. The up-conversion emission intensity of CaNb2O6:Er3+/Yb3+ became the maximum at 5 mol % Er3+ and 20 mol % Yb3+ under excitation at 980 nm.</p>
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 128 (11), 866-874, 2020-11-01
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1391130851447885696
-
- NII論文ID
- 130007934287
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可